Influence of Khat Extract (Catha edulis) on corrosion resistance of Co-Cr dental alloys / Influência do extrato de Khat (Catha edulis) na resistência à corrosão de ligas dentais Co-Cr

Objective: The aim of this experimental study was to assess the effect of khat extract with different concentrations on the corrosion resistance of cobalt-chromium (Co-Cr) dental alloys used for removable denture. Material and Methods:The corrosion resistance of three Co-Cr alloys (Neobond II®, Kera 501® and PD Casta H®) was evaluated in artificial saliva in presence of three different concentrations of khat extracts. Fusayama-Meyer artificial saliva was used as a reference solution. The corrosion properties of the alloys were analyzed using potentiodynamic polarization, electrochemical impedance spectroscopy and surface analysis. The data was presented in means, standard deviations, and related figures. Comparison between the different concentrations was done using 1-way ANOVA test. The surface analysis was performed using scanning electron microscopy (SEM). Results: the results showed that the corrosion resistance of the three alloys tested (Neobond II®, Kera 501® and PD Casta H®) decreased in artificial saliva containing khat extract compared with that of the reference solution. Additionally, the corrosion resistance of the three Co-Cr dental alloys decreased by increasing the concentration of khat extract. Furthermore, the results indicate that Neobond II® alloy showed the least corrosion resistance compared with that of Kera 501® and PD Casta H® alloys. Conclusion: Khat extract with different concentrations had negative impact on the corrosion resistance of Cr-Co alloys. More in-vivo studies are highly recommended to confirm the results of the present study (AU)

Objetivo: O objetivo deste estudo experimental foi avaliar o efeito do extrato de khat em diferentes concentrações na resistência à corrosão de ligas dentárias de cobalto-cromo (Co-Cr) utilizadas em próteses removíveis. Material e Métodos:A resistência à corrosão de três ligas de Co-Cr (Neobond II®, Kera 501® e PD Casta H®) foi avaliada em saliva artificial na presença de três concentrações diferentes de extratos khat. A saliva artificial de Fusayama-Meyer foi usada como solução de referência. As propriedades de corrosão das ligas foram analisadas usando polarização potenciodinâmica, espectroscopia de impedância eletroquímica e análise de superfície. Os dados foram apresentados em médias, desvios-padrão e figuras relacionadas. A comparação entre as diferentes concentrações foi feita usando o teste One-way ANOVA. A análise de superfície foi realizada em microscopia eletrônica de varredura (MEV). Resultados: os resultados mostraram que a resistência à corrosão das três ligas testadas (Neobond II®, Kera 501® e PD Casta H®) diminuiu na saliva artificial contendo extrato khat em comparação com a solução de referência. Além disso, a resistência à corrosão das três ligas dentais Co-Cr diminuiu com o aumento da concentração de extrato de khat. Além disso, os resultados indicam que a liga Neobond II® apresentou a menor resistência à corrosão em comparação com as ligas Kera 501® e PD Casta H®. Conclusão: O extrato de Khat com diferentes concentrações teve impacto negativo na resistência à corrosão de ligas de Cr-Co. Mais estudos in vivo são altamente recomendados para confirmar os resultados do presente estudo. (AU)

Comportamento do titânio comercialmente puro obtido por diferentes processamentos submetidos a soluções fluoretadas / Behavior of commercially pure titanium obtained by different processing under the action of different fluoride solutions

O objetivo deste estudo in vitro foi analisar o comportamento superficial do titânio comercialmente puro (grau 2 ASTM) usinado e obtido pelo processamento de metalurgia do pó sob a ação de diferentes soluções fluoretadas, através da análise do grau de corrosão em microscopia óptica (MO) e da rugosidade superficial. Além disso, o estudo se propôs a comparar essas análises com os resultados obtidos com o titânio fundido da dissertação de mestrado de Barros (2004). Todas as amostras receberam procedimento metalográfico padrão e foram divididas em grupos: Gr.1- saliva artificial com pH 7.0 (controle), Gr.2- gel de flúor fosfato acidulado a 1,23% com pH 3.5, Gr.3- gel de NaF a 2% com pH 6.5, Gr.4- solução de NaF a 0,05% com pH 4.0 e Gr.5- solução de NaF a 0,05% com pH 7.5. As amostras foram expostas a estas soluções por 1, 4, 8 e 16 min, intercaladas com imersão em saliva artificial por 24 h, e depois foram observadas em MO e MEV, a cada intervalo de tempo. As imagens em MO, 100x, foram classificadas através de escores de 0 a 4, conforme o grau de corrosão. A rugosidade foi analisada utilizando o parâmetro Ra. Os resultados da análise de MO foram tratados estatisticamente pelo teste qui-quadrado e da rugosidade pelo teste “F” de Snedecor e de Bonferroni (p<0,05). Nos três tipos de amostras, o Gr2 apresentou a corrosão mais severa, e os Gr.4 e 5 apresentaram os menores graus de corrosão. Entretanto, nas amostras usinadas o Gr5 apresentou uma corrosão menos acentuada em relação ao Gr4. No Gr3 houve um aumento da corrosão em função do tempo, sendo que as amostras fundidas mostraram este aumento mais rapidamente. Houve um aumento significativo na rugosidade superficial no Gr.2 nos três tipos de amostras...

The purpose of this in vitro study was to analyze the superficial behavior of commercially pure titanium (grade 2, ASTM), obtained by milling or powder metallurgical process, under the action of different fluoride solutions through the analysis of corrosion grade under an optical microscope (OM) and superficial roughness. Furthermore the results obtained from such analyses were compared with the ones of cast titanium from Barros’s master’s degree dissertation (2004). All specimens received the standard metallography procedure for titanium, and were divided into the following groups, according to the attack solution received: Gr.1- synthetic saliva with pH 7.0 (control), Gr.2- 1.23% acidulated phosphate fluoride gel with pH 3.5, Gr.3- 2% NaF gel with pH 6.5, Gr.4- 0.05% NaF solution with pH 4.0, and Gr.5- 0.05% NaF solution with pH 7.5. The specimens were exposed to these solutions for 1, 4, 8, and 16 minutes, and between each of these times they were immersed in synthetic saliva for 24 h. The surfaces of samples were observed under OM and SEM at each interval time. The images of 100x in OM were classified by means of scores which ranged from 0 to 4, according to corrosion grade. The rugosity was analyzed using Ra parameter. The results of OM analysis were statistically treated by means of Chi-square test and of rugosity through Snededor “F” test and Bonferroni test (p<0,05). In the three different types of samples, the Gr2 presented the most severe corrosion, and the Gr.4 and 5 showed the smallest corrosion grade. However in the milled samples Gr5 showed a less Sharp corrosion than Gr4. The corrosion grade of Gr3 increased according to time, but the cast specimens showed this increase more quickly...

Comportamento do titânio comercialmente puro obtido por diferentes processamentos submetidos a soluções fluoretadas / Behavior of commercially pure titanium obtained by different processing under the action of different fluoride solutions

O objetivo deste estudo in vitro foi analisar o comportamento superficial do titânio comercialmente puro (grau 2 ASTM) usinado e obtido pelo processamento de metalurgia do pó sob a ação de diferentes soluções fluoretadas, através da análise do grau de corrosão em microscopia óptica (MO) e da rugosidade superficial. Além disso, o estudo se propôs a comparar essas análises com os resultados obtidos com o titânio fundido da dissertação de mestrado de Barros (2004). Todas as amostras receberam procedimento metalográfico padrão e foram divididas em grupos: Gr.1- saliva artificial com pH 7.0 (controle), Gr.2- gel de flúor fosfato acidulado a 1,23% com pH 3.5, Gr.3- gel de NaF a 2% com pH 6.5, Gr.4- solução de NaF a 0,05% com pH 4.0 e Gr.5- solução de NaF a 0,05% com pH 7.5. As amostras foram expostas a estas soluções por 1, 4, 8 e 16 min, intercaladas com imersão em saliva artificial por 24 h, e depois foram observadas em MO e MEV, a cada intervalo de tempo. As imagens em MO, 100x, foram classificadas através de escores de 0 a 4, conforme o grau de corrosão. A rugosidade foi analisada utilizando o parâmetro Ra. Os resultados da análise de MO foram tratados estatisticamente pelo teste qui-quadrado e da rugosidade pelo teste “F” de Snedecor e de Bonferroni (p<0,05). Nos três tipos de amostras, o Gr2 apresentou a corrosão mais severa, e os Gr.4 e 5 apresentaram os menores graus de corrosão. Entretanto, nas amostras usinadas o Gr5 apresentou uma corrosão menos acentuada em relação ao Gr4. No Gr3 houve um aumento da corrosão em função do tempo, sendo que as amostras fundidas mostraram este aumento mais rapidamente. Houve um aumento significativo na rugosidade superficial no Gr.2 nos três tipos de amostras...

The purpose of this in vitro study was to analyze the superficial behavior of commercially pure titanium (grade 2, ASTM), obtained by milling or powder metallurgical process, under the action of different fluoride solutions through the analysis of corrosion grade under an optical microscope (OM) and superficial roughness. Furthermore the results obtained from such analyses were compared with the ones of cast titanium from Barros’s master’s degree dissertation (2004). All specimens received the standard metallography procedure for titanium, and were divided into the following groups, according to the attack solution received: Gr.1- synthetic saliva with pH 7.0 (control), Gr.2- 1.23% acidulated phosphate fluoride gel with pH 3.5, Gr.3- 2% NaF gel with pH 6.5, Gr.4- 0.05% NaF solution with pH 4.0, and Gr.5- 0.05% NaF solution with pH 7.5. The specimens were exposed to these solutions for 1, 4, 8, and 16 minutes, and between each of these times they were immersed in synthetic saliva for 24 h. The surfaces of samples were observed under OM and SEM at each interval time. The images of 100x in OM were classified by means of scores which ranged from 0 to 4, according to corrosion grade. The rugosity was analyzed using Ra parameter. The results of OM analysis were statistically treated by means of Chi-square test and of rugosity through Snededor “F” test and Bonferroni test (p<0,05). In the three different types of samples, the Gr2 presented the most severe corrosion, and the Gr.4 and 5 showed the smallest corrosion grade. However in the milled samples Gr5 showed a less Sharp corrosion than Gr4. The corrosion grade of Gr3 increased according to time, but the cast specimens showed this increase more quickly...